INCONEL
| Grade | UNS | Density | Chemical Composition(%) | Tensile Strength ( Mpa min) | Yield Strength ( Mpa min) | Reduction of Area ,min (%) | Elongation min(%) | Hardness (HRC) | ||||||
| INCONEL 625 | N06625 | 8.44 | Ni | Cr | C | Fe | Mn | Si | S | 827 MPa min | 414 MPa min | …. | 30% min | HRC 35 max |
| 58min | 20.0-23.0 | 0.1max | 2max | 0.5max | 0.5max | 0.015max | ||||||||
| P | Al | Ti | Mo | Nb | ||||||||||
| 0.015max | 0.4max | 0.4max | 8.0-10.0 | 3.15-4.15 | ||||||||||
| INCONEL 718 | N07718 | 8.19 | Ni | Cr | Fe | C | Mn | S | Si | 1275 MPa min | 1034 MPa min | 15% | 12% min | HRC 35-40 |
| 50.0-55.0 | 17.0-21.0 | Remainder | 0.08max | 0.35max | 0.015max | 0.35max | ||||||||
| B | P | Mo | S | Ti | Al | Cu | ||||||||
| 0.006max | 0.015max | 2.8-3.3 | 0.015max | 0.65-1.15 | 0.2-0.8 | 0.3max | ||||||||
| Co | ||||||||||||||
| 1.0max | ||||||||||||||
| INCONEL X-750 | N07750 | 8.28 | Ni | Cr | Fe | C | Mn | S | Si | 1170 MPa min | 790 MPa min | 18% | 18% min | HRC 35max |
| 70min | 14.0-17.0 | 5.0-9.0 | 0.08max | 1.0max | 0.01max | 0.5max | ||||||||
| Cu | Nb | Co | Ti | Al | ||||||||||
| 0.3max | 0.7-1.2 | 1.0max | 2.25-2.75 | 0.4-1.0 | ||||||||||
| INCONEL 600 | N06600 | 8.47 | Ni | Cr | Fe | C | Mn | S | Si | 552 MPa min | 241 MPa min | …. | 30% min | … |
| 72.0min | 14.0-17.0 | 6.0-10.0 | 0.15max | 1.0max | 0.015max | 0.5max | ||||||||
| Cu | ||||||||||||||
| 0.5max | ||||||||||||||
| INCONEL 601 | N06601 | 8.11 | Ni | Cr | Al | Fe | C | Mn | Si | 550 MPa min | 205 MPa min | …. | 40% min | … |
| 58.0-63.0 | 21.0-25.0 | 1.0-1.7 | Remainder | 0.1max | 1.0max | 0.5max | ||||||||
| S | Cu | |||||||||||||
| 0.015max | 1.0max | |||||||||||||